低温脆性温度测定仪-橡胶低温脆性试验机 试样规格：
试样的长度为（20.5±0.5）MM，宽度为（6.0±0.5）MM，厚度为（2.0±0.2）MM.
低温脆性温度测定仪-橡胶低温脆性试验机 试验报告
A 本标准名称或编号
B 样品的详细说明及其来源
C 使用的传热介质、致冷剂或其他降温方式
D 程序A:脆性温度和试样破坏现象
E 程序B：规定的试验温度和试验结果
低温测温计
采用 小分度不大于1度的低温测温计测量冷冻介质的温度，可使用低温温度计、热电偶、电阻温度计等。低温温度计为内标式半浸的，以尾长150MM，浸入液体深度75MM为宜。
升降夹持器
升降夹持器由夹持器和升降装置组成
从试样受冲击部位，到夹持器下端的距离为（11.0加或等于0.5）mm。
Sample specifications:
The length of the sample is (20.5 ± 0.5) mm, the width is (6.0 ± 0.5) mm, and the thickness is (2.0 ± 0.2) mm
test report
Name or number of this standard
Detailed description and source of sample B
The heat transfer medium, refrigerant or other cooling methods used by C
D Program A: Brittle Temperature and Sample Failure Phenomenon
E program B: specified test temperature and test results
Low temperature thermometer
Low temperature thermometers with a minimum division of no more than 1 degree can be used to measure the temperature of the frozen medium, including low-temperature thermometers, thermocouples, resistance thermometers, etc. The low-temperature thermometer is an internal standard semi immersion type, with a tail length of 150mm and a liquid immersion depth of 75mm.
Lift gripper
The lifting gripper consists of a gripper and a lifting device
The distance from the impact site of the specimen to the lower end of the gripper is (11.0 plus or equal to 0.5) mm.
技术参数:
一、1.控温范围：室温 -70℃（室温≤25℃）
二、2.恒温精度：±0.3℃
三、3.降温速度：0℃～﹣30℃ 约2.5℃/min
四、﹣30℃～﹣40℃ 约2.5℃/min
五、﹣40℃～﹣70℃ 约2.0℃/min
六、4. 大外形尺寸：900×500×800mm（长×宽×高）
七、5.工作室有效工作空间：280×170×120mm（长×宽×高）
八、6.可装试样数量：1
九、7.数字计时器数字计时器：0秒 -99分钟，分辨率1秒
十、8.冷却介质：乙醇或其他不冻液
十一、9.搅拌电机：8W
十二、10.工作电源：220V--240V，50Hz，1.5kW
十三、11.工作温度:≤25℃
Technical parameters:
1、 1. Temperature control range: room temperature -70 ℃ (room temperature ≤ 25 ℃)
2、 2. Constant temperature accuracy: ± 0.3 ℃
3、 3. Cooling rate: 0 ℃ to -30 ℃, approximately 2.5 ℃/min
4、 -30 ℃ to -40 ℃, approximately 2.5 ℃/min
5、 -40 ℃ to -70 ℃, approximately 2.0 ℃/min
6、 4. Maximum external dimensions: 900 × 500 × 800mm (length × width × height)
7、 5. Effective workspace in the studio: 280 x 170 x 120mm (length x width x height)
8、 6. Number of samples that can be loaded: 1
9、 7. Digital timer: 0 seconds to 99 minutes, resolution of 1 second
10、 8. Cooling medium: ethanol or other non freezing liquid
11、 9. Mixing motor: 8W
12、 10. Working power supply: 220V -240V, 50Hz, 1.5kW
13、 11. Working temperature: ≤ 25 ℃
使用方法
1接通电源，温控仪和计时器显示灯亮。
2向冷井中注入冷冻介质（一般为工业乙醇），其注入量应保证夹持器的下端到液面的距离为75±10mm。
3将试样垂直夹在夹持器上。夹的不宜过紧或过松，以防止试样变形或脱落。
4按下夹持器，开始冷冻试样，同时启动时序控制开关（或按动秒表）计时。试样冷冻时间规定为3.0±0.5min。试样冷冻期间，冷冻介质温度波动不得超过±1℃。
5提起升降夹持器，使冲击器在半秒钟内冲击试样。
6取下试样，将试样按冲击方向弯曲成180°，仔细观察有无破坏。
7试样经冲击后（每个试样只准冲击一次），如出现破坏时，应提高冷冻介质的温度，否则降低其温度，继续进行试验。 温度，如这两个结果相差不大于1℃时，即试验结束。
注意事项
1在试验过程中不能切断冷却循环，否则会产生不制冷的效果。
2气缸压力在出厂前已调节好，不能任意变动。
Usage method
1. Connect the power supply, and the temperature controller and timer display lights will turn on.
Inject freezing medium (usually industrial ethanol) into the cold well in two directions, and the injection amount should ensure that the distance from the lower end of the clamp to the liquid level is 75 ± 10mm
3. Vertically clamp the sample onto the gripper. The clamp should not be too tight or too loose to prevent deformation or detachment of the sample.
Press the gripper to start freezing the sample, and at the same time, activate the timing control switch (or press the stopwatch) to start timing. The freezing time for the sample is specified as 3.0 ± 0.5min. During the freezing period of the sample, the temperature fluctuation of the freezing medium shall not exceed ± 1 ℃.
Lift the lifting gripper and allow the impactor to impact the specimen within half a second.
Remove the sample and bend it 180 ° in the direction of impact, carefully observing for any damage.
After the impact of 7 samples (each sample is only allowed to be impacted once), if damage occurs, the temperature of the freezing medium should be increased. Otherwise, the temperature should be lowered and the test should continue. When the temperature difference between these two results is no more than 1 ℃, the experiment ends.
Precautions
During the experiment, the cooling cycle cannot be cut off, otherwise it will produce a non cooling effect.
The pressure of cylinder 2 has been adjusted before leaving the factory and cannot be changed arbitrarily.
冲击器
冲击器头部形状和尺寸，冲击器的质量为（200±20）g,其工作行程为（40±1）mm。冲击装置的弹簧在压缩状态下，冲击器端部到试样的距离为（25±1）mm。
低温测温计
采用 小分度不大于1度的低温测温计测量冷冻介质的温度，可使用低温温度计、热电偶、电阻温度计等。低温温度计为内标式半浸的，以尾长150MM，浸入液体深度75MM为宜。
冷冻介质
冷冻介质由适宜的传热介质加致冷剂调配而成。
使用方法
4.1接通电源，温控仪和计时器显示灯亮。
4.2向冷井中注入冷冻介质（一般为工业乙醇），其注入量应保证夹持器的下端到液面的距离为75±10mm。
4.3将试样垂直夹在夹持器上。夹的不宜过紧或过松，以防止试样变形或脱落。
4.4达到试验温度后，按下启动按钮，试验机自动工作（按下夹持器，开始冷冻试样，同时启动时序控制开关或按动秒表计时。试样冷冻时间规定为3.0±0.5min。试样冷冻期间，冷冻介质温度波动不得超过±1℃）
4.5取下试样，将试样按冲击方向弯曲成180°，仔细观察有无破坏。
4.6试样经冲击后（每个试样只准冲击一次），如出现破坏时，应提高冷冻介质的温度，否则降低其温度，继续进行试验。
4.7温度调节方法：a、按set键，温控仪进入设置状态
b、按“＜”键移动到要设置的位置
c、按“∧”键调整温度
d、按“set”键确定
通过反复试验，确定至少有两个试样不破坏的 低温度和至少一个试样破坏的 高温度，如这两个结果相差不大于1℃时，即试验结束。
结构原理
A、本设备由制冷压缩机主机体、加热装置、电子控制箱、冷却槽、冷却介质循环系统、自动报警装置等部分组成。启动制冷开关后，压缩机开始工作，制冷系统进入正式工作状态。制冷压缩机连续不断的工作，当接近设定温度时，冷却槽中的加热装置开始按比例提供热量，用以平衡制冷系统产生的多余冷量，以达到恒温的目的。搅拌可使冷却槽内的冷却介质不断循环，使温度均匀一致。
B、试样夹持器
试样一边夹持4个试样（橡胶类），另一边夹持15个试样（塑料类）。
C、冲击装置
冲击装置由冲击锤和自锁机构组成。
D、冲击器
冲击头半径为1.6±0.1mm；
冲击时，冲击头和试样夹持器之间间隙为6.4±0.3mm；
冲击头的中心线与试样夹持器之间的距离为8±0.3mm。
我厂主要产品有：
拉力材料试验机（符合国标GB/T1172-1999、GB/T2975-1998、GB/T10632-1989）
硫化橡胶耐电压强度试验仪/符合国标GB/T1408-2006、ASTMD149
体积表面电阻率测试仪/符合国标GB/T1410-2006、ASTMD257-99
介电常数介质损耗测试仪/符合国标GB/T1409-2006
塑料球压痕硬度测试仪/符合国标GB/T3398-2008
橡胶塑料摩擦磨损试验机/符合国标GB/T3960-1983
热变形维卡温度测定仪/符合国标GB/T8802-2001
熔体流动速率测定仪/符合国标GB/T3682-2000
水平垂直燃烧试验仪/符合国标GBGB/T5169.16-2002、ANSI/UL94
氧指数测定仪GB/T2406.2-2009GB/T2406.1-2008
垂直燃烧试验机符合国标GB/T18380.11-2008
塑料球压痕硬度计（符合国标GB/T3398-2008）